Electrochemical properties of nanoscale Cu Co spinel ferrite system: A promising positive electrode for high performance supercapacitors
Journal
Journal of Energy Storage
Fecha
2024
Autores
Murugan, A
Siva, V
Shameem, A
Deepika, R
Bharathkumar, S
Asath-Bahadur, S
Resumen
There is an enormous demand for energy storage applications with a high specific capacity, superior energy and power density, and long-life cycles because of the increase in portable electronic appliances. The use of ternary metal oxide electrode materials for energy storage applications in supercapacitors based on multi-redox sites has gained more attention from researchers due to their outstanding specific capacitance and numerous redox sites. Copper cobalt ferrites (CuCoFe2O4) nanoparticles (NPs) have been synthesised by the simple microwave combustion method and employed as a positive electrode material for energy storage in supercapacitors (SCs). To study the physical and electrochemical properties of the prepared nanoparticles by XRD, FTIR, SEM-EDX, HR-TEM, and electrochemical analysis have been carried out. X-ray diffraction planes indicating the cubic spinel structure with a space group of Fd-3m and the crystalline phase purity of the synthesised CuCoFe2O4 NPs were also characterized by Rietveld refinement. HR-TEM analysis of the existing agglomeration of particles and SAED pattern shows the excellent crystalline nature of the materials. The CuCoFe2O4 electrode obtained an outstanding specific capacitance of 237.5 F g−1 at 0.5 A g−1 current density in a 3 M KOH electrolyte in a standard three-electrode system. Further fabricated of a solid-state asymmetric supercapacitor (ASC) device by using CuCoFe2O4 NPs and activated carbon (AC) as the positive and negative electrodes, respectively. This ASC device offers a superior energy density value of 16 Wh kg−1 and a power density of 8048 W kg−1. In addition, the ASCs device exhibits cycle stability of 82 % after 10,000 GCD charge and discharge cycles at a current density of 40 A g−1, displaying its high cycling stability.